Pre-alloyed Powder FeCuSn (X5-506) Description
Pre-alloyed Powder FeCuSn (X5-506) is manufactured by atomization method. Since each powder particle contains various metal elements that make up the alloy, the composition uniformity of the pre-alloyed powder is quite good.
Since pre-alloying greatly reduces the activation energy required for the diffusion of metal atoms during the sintering process, the sintering performance is good, and the sintering temperature is low. Therefore, it can reduce the amount of graphite molds used and the power consumption. Under the same cutting performance, the use of pre-alloyed powder can reduce the diamond concentration by 15% to 20%, significantly reducing the cost of diamond tools.
Pre-alloyed Powder FeCuSn (X5-506) Specifications
|
Specification
|
|
Sintering Temperature (℃)
|
820
|
|
Oxygen Content (%)
|
≤0.30
|
|
Carcass Hardness
|
95-105HRB
|
|
Theoretical Density (g/cm3)
|
8.15
|
|
Bulk Density (g/cm3)
|
3.5
|
|
Bending Strength (Mpa)
|
1100-1300
|
Pre-alloyed Powder FeCuSn (X5-506) Applications
Pre-alloyed Powder FeCuSn (X5-506) greatly improves the performance of diamond tools and significantly reduces the cost of diamond tools. It is suitable for the sintering of small saw blades, medium-diameter saw blades for medium-soft granite, mining cutter heads, etc.