Pre-alloyed Powder FeCuNiSn (X6-620) Description
Pre-alloyed Powder FeCuNiSn (X6-620) is manufactured by atomization method. Since each powder particle contains various metal elements that make up the alloy, the composition uniformity of the pre-alloyed powder is quite good.
This powder has a low sintering temperature, which can effectively reduce sintering loss, reduce the amount of elemental tin, and reduce production costs. The carcass has a high degree of alloying, which can improve the overall performance of the carcass.
Pre-alloyed Powder FeCuNiSn (X6-620) Specifications
|
Specification
|
|
Sintering Temperature (℃)
|
800
|
|
Oxygen Content (%)
|
≤0. 25
|
|
Carcass Hardness
|
100-110 HRB
|
|
Theoretical Density (g/cm3)
|
8.08
|
|
Bulk Density (g/cm3)
|
3.3
|
|
Bending Strength (Mpa)
|
1200-1500
|
Pre-alloyed Powder FeCuNiSn (X6-620) Applications
Pre-alloyed Powder FeCuNiSn (X6-620) is suitable for small saw blades for wall grooves, medium-diameter saw blades for stone and concrete, and grinding products such as grinding discs, grinding blocks, and hobs.